Mobilgrease 28
Synthetic Aviation Grease
Product Description
Mobilgrease 28 is a supreme performance, wide-temperature, antiwear grease designed to combine the unique features of a polyalphaolefin (PAO) synthetic base fluid with an organo-clay (non-soap) thickener. Its consistency is between an NLGI No. 1 and No. 2 grease. It offers outstanding performance over a wide temperature range. The wax-free nature of the synthetic base fluid, together with its high viscosity index compared to mineral oils, provide excellent low temperature pumpability, very low starting and running torque, and can help reduce operating temperatures in the load zone of rolling element bearings.
The clay thickener gives Mobilgrease 28 a high dropping point value of around 300ºC, which provides excellent stability at high temperatures. Mobilgrease 28 resists water washing, provides superior load-carrying ability, reduces frictional drag, and prevents excessive wear. Tests show that Mobilgrease 28 lubricates effectively rolling element bearings under conditions of high speeds and temperatures. Mobilgrease 28 has also shown excellent ability to lubricate heavily loaded sliding mechanisms, such as wing flap screw jacks.
For more than 30 years, Mobilgrease 28 has been the multi-purpose grease of choice for military and related aviation applications, worldwide.
Applications
Mobilgrease 28 is designed for the lubrication of plain and rolling bearings at low to high speeds, and splines, screws, worm gears, and other mechanisms where high friction reduction, low wear, and low lubricant friction losses are required. The recommended operating temperature range is -54ºC to 177ºC (-65ºF to 350ºF) with appropriate relubrication intervals.
Mobilgrease 28 is recommended for use in landing wheel assemblies, control systems and actuators, screw jacks, servo devices, sealed-bearing motors, oscillating bearings, and helicopter rotor bearings on military and civil aircraft. Subject to equipment manufacturer approvals, it can also be used on naval shipboard auxiliary machinery and where superseded specifications MIL-G-81322 (WP), MIL-G-7711A, MIL-G-3545B, and MIL-G-25760A are recommended.
Mobilgrease 28 is also recommended for industrial lubrication, including sealed or repackable ball and roller bearings wherever extreme temperature conditions, high speeds, or water washing resistance are factors. Typical industrial applications include conveyor bearings, small alternator bearings operating at temperatures near 177ºC (350ºF), high-speed miniature ball bearings, and bearing applications where oscillatory motion, and vibration create problems.
Mobilgrease 28 is qualified by the U.S. Military under Specification MIL-PRF-81322, General-Purpose, Aircraft, and Specification DOD-G-24508A (Navy) for shipboard auxiliary machinery. It is a U.S. Military Symbol WTR and NATO Code Number G-395 grease.
Specifications and Approvals
Mobilgrease 28
Is Approved Against
Quality Level
| MIL-PRF-81322G | X | | |
| DOD-G-24508A, Amendment 4 | | X | |
| NATO G-395 | X | |
Typical Properties
Test Methods
Mobilgrease 28 Typicals (1)
MIL-PRF-81322 Limits
| NLGI Grade | | 1 1/2 | |
| Thickener Type | | Clay (non-soap) | |
| Color | Visual | Dark Red | |
| Structure | Visual | Smooth, buttery | |
| Dropping Point, ºC (ºF) | ASTM D 2265 | 307 (584) | 232 (450) min |
| Viscosity of Base Oil, cSt | ASTM D 445 | | |
| at 40ºC | | 30 | |
| at 100ºC | | 5.7 | |
| Low Temp. Torque at -54ºC (-65ºF), Nm (g-cm) | ASTM D 1478 | | |
| Starting | | 0.43(4400) | 0.98 (10,000) max |
| Running, after 1 Hr | | 0.05 (510) | 0.098 (1,000) max |
| Penetration @ 25ºC (77ºF), 60 Stoke Worked, mm/10 | ASTM D 217 | 293 | 265-320 |
| Extended Worked Penetration Stability, 100,000 Strokes, mm/10 | FTM 313 | 303 | 350 max |
| Oil Separation, 30 Hrs at 177ºC, wt % | ASTM D 6184 | 3.5 | 2.0 - 8.0 |
| Evaporation Loss, 22 Hrs at 177ºC, wt % | ASTM D 2595 | 6 | 10 max |
| Copper Strip Corrosion, 24 Hrs at 100ºC | ASTM D 4048 | 1b | 1b max |
| Four-Ball Wear, Scar dia, mm | ASTM D 2266 | 0.6 | 0.8 max |
| Load Wear Index, kgf | ASTM D 2596 | 40 | 30 min |
| Rust Protection, 48 Hrs at 125ºF, › 1mm dia Corrosion Spots | ASTM D 1743 | Pass | 0 |
| Water Washout, 1 Hr at 41ºC, wt % | ASTM D 1264 | 1 | 20 max |
| High Temperature Performance, Hrs at 177ºC | ASTM D 3336 (modified) | Pass | 400 min |
| Oxidation Stability, pressure drop in kPa | ASTM D 942 | | |
| 100 Hrs at 99ºC | | Pass | 83 max |
| 500 Hrs at 99ºC | | Pass | 172 max |
| Dirt Count, Particles/mL | FTM 3005 | | |
| 25-74 Micron | | Pass | 1000 max |
| 75 Micron or Larger | | 0 | 0 |
| Oscillation Friction and Wear, Scar Dia, 35,000 cycles, 90º Angle, Aluminum Bronze Block, mm | Modified ASTM D 3704 | Pass | 6.35 max |
| Rubber Swell, L Type Synthetic, 1 week at 70ºC (158ºF), vol % | FTM 3603 | 6 | 10 max |
| (1) Typical properties are typical of those obtained with normal production tolerance and may vary slightly, while remaining within specified limits. | | | |